In general, 鋼 is referred to as 'Carbon Steel' where the main alloying component used is Carbon and when no other elemental requirement is specified; i.e., Chromium, Cobalt, Nickel. Carbon Steel can be divided into two categories as, high and low Carbon Steel. Just as the names suggests, High carbon steel contains a higher amount of carbon, and low carbon steel contains a low percentage of carbon. Mild Steel is a form of low Carbon Steel. The 主な違い between Carbon Steel and Mild Steel is that 炭素鋼 炭素量が多い whereas 軟鋼 炭素の量が比較的少ないです。
炭素鋼とは
Usually, Carbon Steel contains about 0。05-1.70重量パーセントの炭素. Increasing the carbon percentage in steel gives it additional strength and it is also considered as the most economical approach of increasing the strength of steel. However, as a result of adding more carbon, the steel also tends to become brittle and less ductile. Therefore, the right balance of carbon has to be added in order to achieve extra performing steel. 高炭素鋼 has a 0.3-1.70パーセントの間の炭素含有量, and 低炭素鋼 has a 炭素含有量0.05-0.15パーセント。 低炭素鋼は、製造価格が比較的低いため、今日使用されている最も一般的なタイプの鋼です。
高炭素鋼は低炭素鋼よりも熱処理が容易であるため、多くの用途で非常に役立ちます。 他の元素不純物も鋼に非常に興味深い特性をもたらす可能性があります。 すなわち硫黄。 高鋼炭素の一般的な用途には、次のものがあります。 レール鋼、プレ-ストレスコンクリート、ワイヤーロープ、タイヤ補強材、ナイフ、鋸刃、歯車、チェーンなど。
軟鋼とは
軟鋼は最も穏やかなタイプの炭素鋼であり、炭素の量が比較的少ないです。 軟鋼には、マンガン、シリコン、微量のリンなどの他の元素も含まれている可能性があります。 これらの追加要素は、鉄結晶内の転位を防ぐことにより、金属鉄の構造の完全性を保護します。 炭素は硬化剤として機能し、添加される炭素の割合は鋼の強度に正比例します。 鋼の強度は、一般に、添加された炭素の割合とともに増加します。
軟鋼は最も普及している鋼の形態であり、米国だけですべての鋼製品の85％に使用されています。 延性、強度、経済的な価格などの望ましい特性により、人気のある鉄の形態になりました。 軟鋼は、ワイヤー、鋼板、その他の建築材料の製造によく使用されます。
炭素鋼と軟鋼の違い
意味
In general, 炭素鋼 has a higher amount of carbon.
軟鋼 has a relatively low amount of carbon.
炭素含有量
炭素鋼 0.05-1.70パーセントの範囲の炭素の重量パーセントを持つことができます。
軟鋼 has a carbon content of 0.05-0.25 percent by weight.
価格
炭素鋼 より高価です。
軟鋼 安いです
プロパティ
炭素鋼 is stronger than Mild Steel. It is also brittle and can break easily when compared to Mild Steel.
軟鋼 その柔らかくて弱い特性のために、さまざまな形状に簡単に溶接することができます。
熱処理
炭素鋼 熱処理に成功することができます。
軟鋼 熱処理に成功することはできません。